Gunning Material for Converter
- 10275.31 THB/t. - from 27 t.
- In detail
ZMPL - 1(magnesia), ZMPL - 2(magnesia), ZMPL - 3(magnesia)
ZGPL - 1(olivine), ZGPL - 2(olivine), ZGPL - 3(olivine)
ZBPL - 1(magnesia dolomite), ZBPL - 2(magnesia doclomite)
Production Technics: it is produced by mixing with fine quality magnesia, calcined olivine and high purified compound magnesia dolomite as the main rawmaterial, and adding various compound anchoring agent. Due to using high purified raw material and compound anchoring agent, the adhesive rate of this serial products can reach to above 95% and having good erosion resisting and heat stability, it is the ideal gunning material for rotary furnace main surface and slag line.
Main Use: high temperature gunning for converter main surface, slag line and trunnion part.
Usage Method: These serial products are suitable for any type of gunning devices,12% - 16% of water content needqs to beaddqed during using, the gunning thickness is around 20mm - 30mm each time Which can be used for 8 to 12 heats.